ASTM B997-15
Standard Specification for Zinc-Aluminum Alloys in Ingot Form for Hot-Dip Coatings
Automatische name übersetzung:
Standard-Spezifikation für Zink -Aluminium-Legierungen in Blockform für Hot - Dip Coatings
NORM herausgegeben am 1.6.2015
Informationen über die Norm:
Bezeichnung normen: ASTM B997-15
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.6.2015
SKU: NS-609971
Zahl der Seiten: 3
Gewicht ca.: 9 g (0.02 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Die Annotation des Normtextes ASTM B997-15 :
Keywords:
GALFAN, hot-dip coating alloy, zinc-5 % aluminum alloy, zinc-10 % aluminum alloy, zinc-15 % aluminum alloy,, ICS Number Code 77.150.60 (Lead, zinc and tin products)
Ergänzende Informationen
| 1. Scope | ||||||||||||||||||||
|
1.1 This specification covers certain zinc-aluminum (Zn-Al) alloys in ingot form for re-melting for use in the production of hot-dip coatings on steel. Alloy compositions are specified below and in Table 1.
Note 1: The zinc-aluminum alloys in Specification B997 are intended to be used primarily to
create a molten zinc-aluminum bath and differ from the master
alloys in Specification B860
which are intended primarily to adjust the concentration of certain
elements in molten zinc galvanizing baths.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||||||||
| 2. Referenced Documents | ||||||||||||||||||||
|