ASTM D5379/D5379M-98
Standard Test Method for Shear Properties of Composite Materials by the V-Notched Beam Method
Automatische name übersetzung:
Standard Test Method for Schereigenschaften von Verbundwerkstoffen durch die V- Kerb -Methode
NORM herausgegeben am 10.12.1998
Informationen über die Norm:
Bezeichnung normen: ASTM D5379/D5379M-98
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 10.12.1998
SKU: NS-30949
Zahl der Seiten: 13
Gewicht ca.: 39 g (0.09 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Die Annotation des Normtextes ASTM D5379/D5379M-98 :
Keywords:
Composites, High modulus fibrous composites, In-plane shear properties, Interlaminar shear strength, Laminates, Notch testing, Polymers-composites, Shear testing-aerospace materials, Shear testing-shear modulus, V-notched beam method, ICS Number Code 83.140.20 (Laminated sheets)
Ergänzende Informationen
| 1. Scope | ||||||||||||||||||||||||||||||||||
|
1.1 This test method determines the shear properties of composite materials reinforced by high-modulus fibers. The composite materials are limited to continuous-fiber or discontinuous-fiber reinforced composites in the following material forms: 1.1.1 Laminates composed only of unidirectional fibrous laminae, with the fiber direction oriented either parallel or perpendicular to the loading axis. 1.1.2 Laminates composed only of woven-fabric filamentary laminae with the warp direction oriented either parallel or perpendicular to the loading axis. 1.1.3 Laminates composed only of unidirectional fibrous laminae, containing equal numbers of plies oriented at 0 and 90° in a balanced and symmetric stacking sequence, with the 0° direction oriented either parallel or perpendicular to the loading axis. 1.1.4 Short-fiber reinforced composites with a majority of the fibers being randomly distributed. Note 1-This shear test concept was originally developed without reference to fiber direction for use on isotropic materials such as metals or ceramics.1.2 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text the inch-pound units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard. |
||||||||||||||||||||||||||||||||||
| 2. Referenced Documents | ||||||||||||||||||||||||||||||||||
|
Empfehlungen:
Aktualisierung der technischen Normen
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.