Standard Test Method for Notch Tensile Test to Measure the Resistance to Slow Crack Growth of Polyethylene Pipes and Resins
Name übersetzen
NORM herausgegeben am 1.2.2018
Bezeichnung normen: ASTM F1473-18
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.2.2018
SKU: NS-809956
Zahl der Seiten: 7
Gewicht ca.: 21 g (0.05 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
fracture, notch testing, pipes, polyethylene, resin, slow crack growth ,, ICS Number Code 23.040.20 (Plastic pipes)
Significance and Use | ||||||
5.1 This test method is useful to measure the slow crack growth resistance of molded plaques of polyethylene materials at accelerated conditions such as 80°C, 2.4-MPa stress, and with a sharp notch. 5.2 The testing time or time to failure depends on the following test parameters: temperature; stress; notch depth; and specimen geometry. Increasing temperature, stress, and notch depth decrease the time to failure. Material parameters, not controlled by the laboratory, that could impact the test results (time to failure) are: pigment (color or carbon black) and the carrier resin for the pigment, or both. Thus, in reporting the test time or time to failure, all the conditions of the test shall be specified. Note 3: Time to failure can also be affected by the degree of
pigment (color or carbon black) dispersion and distribution within
the test specimen. Test Method D5596 and ISO 18553 provide methods for
assessing the degree of dispersion and distribution of the
pigment
|
||||||
1. Scope | ||||||
1.1 This test method determines the resistance of polyethylene materials to slow crack growth under conditions specified within. Note 1: This test method is known as PENT (Pennsylvania Notch
Test) test.
1.2 The test is generally performed at 80°C and at 2.4 MPa, but may also be done at temperatures below 80°C and with other stresses low enough to preclude ductile failure and thereby eventually induce brittle type of failure. Generally, polyethylenes will ultimately fail in a brittle manner by slow crack growth at 80°C if the stress is below 2.4 MPa. 1.3 The test method is for specimens cut from compression molded plaques.2 See Appendix X1 for information relating to specimens from pipe. 1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||
2. Referenced Documents | ||||||
|
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-04-25 (Zahl der Positionen: 2 896 007)
© Copyright 2024 NORMSERVIS s.r.o.