Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments (Includes all amendments And changes 12/31/2010).
Automatische name übersetzung:
Standard Test Method for Mechanical Wasserstoffversprödung Bewertung der Plating / Coating Prozesse und Service-Umgebungen
NORM herausgegeben am 1.7.2006
Bezeichnung normen: ASTM F519-06e2
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.7.2006
SKU: NS-55599
Zahl der Seiten: 17
Gewicht ca.: 51 g (0.11 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
cleaner, coating, delayed failure, fluids, hydrogen embrittlement, maintenance chemicals, plating/coating, steel, stress cracking, threshold, ICS Number Code 25.220.40 (Metallic coatings)
1. Scope | ||||||||||||||||||||||||||||||||||||||||||||||||||||
1.1 This test method describes mechanical test methods and defines acceptance criteria for coating and plating processes that can cause hydrogen embrittlement in steels. Subsequent exposure to chemicals encountered in service environments, such as fluids, cleaning treatments or maintenance chemicals that come in contact with the plated/coated or bare surface of the steel, can also be evaluated. 1.2 This test method is not intended to measure the relative susceptibility of different steels. The relative susceptibility of different materials to hydrogen embrittlement may be determined in accordance with Test Method F 1459 and Test Method F 1624. 1.3 This test method specifies the use of air melted AISI E4340 steel per SAE AMS-S-5000 (formerly MIL-S-5000) heat treated to 260 - 280 ksi (pounds per square inch x 1000) as the baseline. This combination of alloy and heat treat level has been used for many years and a large database has been accumulated in the aerospace industry on its specific response to exposure to a wide variety of maintenance chemicals, or electroplated coatings, or both. Components with ultimate strengths higher than 260 - 280 ksi may not be represented by the baseline. In such cases, the cognizant engineering authority shall determine the need for manufacturing specimens from the specific material and heat treat condition of the component. Deviations from the baseline shall be reported as required by section . The sensitivity to hydrogen embrittlement shall be demonstrated for each lot of specimens as specified in section . 1.4 Test procedures and acceptance requirements are specified for seven specimens of different sizes, geometries, and loading configurations. 1.5 Pass/Fail RequirementsFor plating/coating processes, specimens must meet or exceed 200 h using a sustained load test (SLT) at the levels shown in . 1.5.1 The loading conditions and pass/fail requirements for service environments are specified in . 1.5.2 If approved by the cognizant engineering authority, a quantitative, accelerated ( 24 h) incremental step-load (ISL) test as defined in may be used as an alternative to SLT. 1.6 This test method is divided into two parts. The first part gives general information concerning requirements for hydrogen embrittlement testing. The second is composed of annexes that give specific requirements for the various loading and specimen configurations covered by this test method (see section for a list of types) and the details for testing service environments. 1.7 The values stated in the foot-pound-second (fps) system in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||||||||||||||||||||||||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||||||||||||||||||||||||||||||||||||
|
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-05-17 (Zahl der Positionen: 2 902 148)
© Copyright 2024 NORMSERVIS s.r.o.